Water Based
Water Based
Industrial PSA
Compared with solvent-based acrylic PSAs, water-based acrylic PSAs generally have the drawbacks of significantly lower adhesive properties such as initial adhesive strength, peeling strength, and holding power, and a slower drying speed.
However, CS Chemical’s water-based acrylic PSAs are environmentally superior without the use of nonylphenyl-based emulsifiers, and do not reduce weather resistance due to emulsifiers and migration. It has the characteristics of good initial adhesion and holding power, and good water and weather resistance.
CS-777
VOCs emission is very low as an water based PSA.
Used for various foams(PU foam, PE foam, EVA foam, EPDM foam, etc.) for the purpose of sound absorption, heat insulation, etc.
| Product name | CS-777 | |
| Substrate | 50μm PET film | |
| Cross Linker | - | |
| Thickness | 50μm | |
| Aging | Room temperature 1day | |
| Ball tack | #9~10 | |
| Adhesive
Strength
(gf/25mm) 180° Peel After 60 min of attachment | SUS 304 | 2050 |
| PE | 500 | |
| ABS | 2100 | |
| PC | 2200 | |
| PVC | 2250 | |
| Glass | 1700 | |
| Holding power (40℃×1kg×1hr) | 1mm < | |
CS-888
VOCs emission is very low as an water based PSA.
It is a product line with workability suitable for the production of industrial double-sided tape. It can be applied to various supports (non-woven fabrics and paper) and has high adhesion and stable heat resistance.
| Product name | CS-888 | |
| Substrate | 50μm PET film | |
| Cross Linker | - | |
| Thickness | 50μm | |
| Aging | Room temperature 1day | |
| Ball tack | #9~10 | |
| Adhesive
Strength
(gf/25mm) 180° Peel After 60 min of attachment | SUS 304 | 2100 |
| PE | 550 | |
| ABS | 2150 | |
| PC | 2200 | |
| PVC | 2200 | |
| Glass | 1900 | |
| Holding power (40℃×1kg×1hr) | 1mm < | |
CS-30
VOCs emission is very low as an water based PSA.
In 2006 water-based PSA for HMC wire harness was first applied in Korea, and it is excellent in curved surface bonding. Currently, we are supplying a stable supply to automobile module manufacturers and automobile manufacturers.
| Product name | CS-30 | |
| Substrate | 50μm PET film | |
| Cross Linker | - | |
| Thickness | 50μm | |
| Aging | Room temperature 1day | |
| Ball tack | #8~9 | |
| Adhesive
Strength
(gf/25mm) 180° Peel After 60 min of attachment | SUS 304 | 1950 |
| PE | 600 | |
| ABS | 2400 | |
| PC | 2650 | |
| PVC | 2600 | |
| Glass | 1650 | |
| Holding power (40℃×1kg×1hr) | 1mm < | |